Injection-molded body and production method therefor

ABSTRACT

Provided is an injection molded article containing a copolymer containing tetrafluoroethylene unit and a fluoro(alkyl vinyl ether) unit, wherein the content of the fluoro(alkyl vinyl ether) unit of the copolymer is 3.9 to 4.8% by mass with respect to the whole of the monomer units, the melt flow rate at 372° C. of the copolymer is 11.0 to 19.0 g/10 min, the melting point of the copolymer is 296 to 305° C., and the amount of fluorine ions dissolving out from the injection molded article into water is 7,500 μg/m2 or lower.

CROSS-REFERENCE TO RELATED APPLICATIONS

This application is a Rule 53(b) Continuation of International Application No. PCT/JP2022/003661 filed Jan. 31, 2022, which claims priorities based on Japanese Patent Application No. 2021-031087 filed Feb. 26, 2021, Japanese Patent Application No. 2021-031090 filed Feb. 26, 2021, Japanese Patent Application No. 2021-031091 filed Feb. 26, 2021, Japanese Patent Application No. 2021-031094 filed Feb. 26, 2021, and Japanese Patent Application No. 2021-162163 filed Sep. 30, 2021, the respective disclosures of which are incorporated herein by reference in their entirety.

TECHNICAL FIELD

The present disclosure relates to an injection molded article and a method for producing the same.

BACKGROUND ART

Patent Document 1 describes an ozone-resistant injection molded article comprising a perfluororesin, wherein the perfluororesin is composed of a perfluoro polymer, has an MIT value of 300,000 cycles or more, and has not more than 50 unstable end groups per 1×10⁶ carbon atoms in the perfluoro polymer.

RELATED ART Patent Document

-   Patent Document 1: International Publication No. WO 2003/048214

SUMMARY

According to the present disclosure, there is provided an injection molded article comprising a copolymer comprising tetrafluoroethylene unit and a fluoro(alkyl vinyl ether) unit, wherein the content of the fluoro(alkyl vinyl ether) unit of the copolymer is 3.9 to 4.8% by mass with respect to the whole of the monomer units, the melt flow rate at 372° C. of the copolymer is 11.0 to 19.0 g/10 min, the melting point of the copolymer is 296 to 305° C., and the amount of fluorine ions dissolving out from the injection molded article into water is 7,500 μg/m² or lower.

Effects

According to the present disclosure, there can be provided an injection molded article which is excellent in physical properties such as the transparency, the rigidity on heating, the long-time tensile creep property, the deterioration resistance to repeated loads, the abrasion resistance at 150° C., the chemical solution low permeability, the heat distortion resistance after chemical immersion and the swelling resistance to chemical solutions, and has a largely improved ozone resistance.

BRIEF DESCRIPTION OF DRAWING

The FIGURE is a plane view, a cross-sectional view, and a side view of the shape of joints prepared in Experimental Examples and Comparative Examples.

DESCRIPTION OF EMBODIMENTS

Hereinafter, specific embodiments of the present disclosure will be described in detail, but the present disclosure is not limited to the following embodiments.

Patent Document 1 proposes, in particular, as an article excellent in the ozone resistance such as a piping member or a joint used in a semiconductor production apparatus, an ozone-resistant injection molded article comprising a perfluororesin, wherein the perfluororesin is composed of a perfluoro polymer, has an MIT value of 300,000 cycles or more, and has not more than 50 unstable end groups per 1×10⁶ carbon atoms in the perfluoro polymer.

Further, it is described in Example 4 in Patent Document 1 that, when a cap nut is prepared by injection molding using a tetrafluoroethylene/perfluoro(propyl vinyl ether) copolymer having a melt flow rate (MFR) of 14.8 g/10 min and the cap nut is subjected to an ozone exposure test, more than 10 cracks are generated after 90 days. Such a cap nut has sufficient ozone resistance, but if an injection molded article having a further improved ozone resistance can be obtained, a longer service life of parts can be achieved, which can result in the reduction of cost.

The present inventors have made intensive studies to solve the problem and found that an injection molded article produced by using a copolymer having a relatively high MFR of about 14.8 g/10 min tends to be more inferior in the ozone resistance than an injection molded article produced by using a copolymer having a relatively low MFR. Then, in addition to the configuration of the copolymer used in injection molding, injection conditions have been largely reconsidered, and as a result, the present inventors have found that the ozone resistance of the injection molded article is largely improved when the amount of fluorine ions dissolving out from the injection molded article into water is low, even by using a copolymer having a relatively high MFR of about 14.8 g/10 min, thereby completing the injection molded article of the present disclosure.

That is, the injection molded article of the present disclosure is an injection molded article containing a specific copolymer, wherein the amount of fluorine ions dissolving out from the injection molded article into water is 7,500 μg/m² or lower. The injection molded article of the present disclosure, due to having such a configuration, is excellent in physical properties such as the transparency, the rigidity on heating, the long-time tensile creep property, the deterioration resistance to repeated loads, the abrasion resistance at 150° C., the chemical solution low permeability, the heat distortion resistance after chemical immersion and the swelling resistance to chemical solutions, and is also excellent in the ozone resistance.

In addition, the injection molded article of the present disclosure has an effect of hardly generating forming defects such as cobwebbing that may be caused in the production by injection molding. Further, even when the injection molded article of the present disclosure has a hollow, the surface roughness is hardly observed on the inside surface of the hollow, and the injection molded article has a predetermined shape.

The amount of fluorine ions dissolving out from the injection molded article into water is 7,500 μg/m² or lower, and since the ozone resistance of the injection molded article can further be improved, preferably 5,500 μg/m² or lower, still more preferably 5,000 μg/m² or lower, and especially preferably 4,500 μg/m² or lower. The lower limit of the amount of fluorine ions dissolving out is not limited, and for example, may be 100 μg/m² or higher, and 500 μg/m² or higher, but the lower, the more preferable.

The amount of fluorine ions dissolving out from the injection molded article into water can be specified by immersing the injection molded article in water at 121° C. for 1 hour, and thereafter, measuring the fluorine ion concentration of the recovered water using a fluorine ion meter, and calculating the amount of fluorine ions dissolving out per surface area of the injection molded article.

The present inventors have made intensive studies and found that, when the amount of fluorine ions dissolving out from the injection molded article is low and the amount of metal dissolving out from the injection molded article into 50% by mass hydrofluoric acid is low, the injection molded article exhibits a further improved ozone resistance.

Since the ozone resistance of the injection molded article can further be improved, the amount of metal dissolving out from the injection molded article into 50% by mass hydrofluoric acid is preferably 200 μg/m² or lower, more preferably 150 μg/m² or lower, still more preferably 100 μg/m² or lower, and especially preferably 50 μg/m² or lower. The lower limit of the amount of metal dissolving out is not limited, and for example, may be 0.1 μg/m² or higher, 0.5 μg/m² or higher, 1.0 μg/m² or higher, and 5 μg/m² or higher, but the lower, the more preferable.

In the present disclosure, the amount of metal dissolving out is the total amount of iron, chrome, and nickel dissolving out from the injection molded article into 50% by mass hydrofluoric acid. The amount of metal dissolving out from the injection molded article into 50% by mass hydrofluoric acid can be specified by immersing the injection molded article in 50% by mass hydrofluoric acid at 25° C. for 24 hours, then measuring the metal concentration in the solution for measurement prepared from the recovered 50% by mass hydrofluoric acid using an ICP emission analyzer, and calculating the amount of metal dissolving out per surface area of the injection molded article.

The injection molded article having an amount of fluorine ions dissolving out and an amount of metal dissolving out within the above ranges can be produced by carrying out the method for producing an injection molded article described below using a specific copolymer.

The injection molded article of the present disclosure contains a copolymer containing tetrafluoroethylene (TFE) unit and a fluoro(alkyl vinyl ether) (FAVE) unit. The copolymer is a melt-fabricable fluororesin. Being melt-fabricable means that a polymer can be melted and processed by using a conventional processing device such as an extruder or an injection molding machine.

Examples of the FAVE constituting the above FAVE unit include at least one selected from the group consisting of a monomer represented by the general formula (1):

CF₂═CFO(CF₂CFY¹O)_(p)—(CF₂CF₂CF₂O)_(q)—Rf  (1)

wherein Y¹ represents F or CF₃, and Rf represents a perfluoroalkyl group having 1 to 5 carbon atoms; p represents an integer of 0 to 5; and q represents an integer of 0 to 5, and a monomer represented by the general formula (2):

CFX═CXOCF₂OR¹  (2)

wherein X is the same or different and represents H, F or CF₃; R¹ represents a linear or branched fluoroalkyl group having 1 to 6 carbon atoms which may contain one or two atoms of at least one selected from the group consisting of H, Cl, Br and I, or a cyclic fluoroalkyl group having 5 or 6 carbon atoms which may contain one or two atoms of at least one selected from the group consisting of H, Cl, Br and I.

Among them, the above FAVE is preferably the monomer represented by the general formula (1), more preferably at least one selected from the group consisting of perfluoro(methyl vinyl ether), perfluoro(ethyl vinyl ether) (PEVE) and perfluoro(propyl vinyl ether) (PPVE), still more preferably at least one selected from the group consisting of PEVE and PPVE, and particularly preferably PPVE.

The content of the FAVE unit of the copolymer is 3.9 to 4.8% by mass with respect to the whole of the monomer units. The content of the FAVE unit of the copolymer is preferably 4.0% by mass or higher, and more preferably 4.1% by mass or higher, and preferably 4.7% by mass or lower, more preferably 4.6% by mass or lower, and still more preferably 4.5% by mass or lower. When the content of the FAVE unit of the copolymer is too low, the ozone resistance, the deterioration resistance to repeated loads, the abrasion resistance at 150° C., the transparency and the heat distortion resistance after chemical immersion of the injection molded article deteriorate. When the content of the FAVE unit of the copolymer is too high, the long-time tensile creep property, the chemical solution low permeability, the rigidity on heating and the swelling resistance to chemical solutions deteriorate. When the content of the FAVE unit of the copolymer is too high, a phenomenon in which the copolymer is elongated from a nozzle like a fiber (cobwebbing) easily occurs in the production of an injection molded article.

The content of the TFE unit of the copolymer is, with respect to the whole of the monomer units, preferably 95.2 to 96.1% by mass, more preferably 95.3% by mass or higher, and still more preferably 95.4% by mass or higher, and especially preferably 95.5% by mass or lower, more preferably 96.0% by mass or lower, and still more preferably 95.9% by mass or lower. When the content of the TFE unit of the copolymer is too high, the ozone resistance, the deterioration resistance to repeated loads, the abrasion resistance at 150° C., the transparency and the heat distortion resistance after chemical immersion of the injection molded article may deteriorate. When the content of the TFE unit of the copolymer is too low, the long-time tensile creep property, the chemical solution low permeability, the rigidity on heating and the swelling resistance to chemical solutions deteriorate. When the content of the TFE unit of the copolymer is too low, a phenomenon in which the copolymer elongates from a nozzle like a fiber (cobwebbing) easily occurs in the production of an injection molded article.

In the present disclosure, the content of each monomer unit in the copolymer is measured by a ¹⁹F-NMR method.

The copolymer can also contain a monomer unit originated from a monomer copolymerizable with TFE and FAVE. In this case, the content of the monomer unit copolymerizable with TFE and FAVE is, with respect to the whole of the monomer units of the copolymer, preferably 0 to 2.0% by mass, more preferably 0.05 to 0.9% by mass, and still more preferably 0.1 to 0.3% by mass.

The monomers copolymerizable with TFE and FAVE may include hexafluoropropylene (HFP), vinyl monomers represented by CZ¹Z²═CZ³ (CF₂)_(n)Z⁴ wherein Z¹, Z² and Z³ are identical or different, and represent H or F; Z⁴ represents H, F or Cl; and n represents an integer of 2 to 10, and alkyl perfluorovinyl ether derivatives represented by CF₂═CF—OCH₂—Rf¹ wherein Rf¹ represents a perfluoroalkyl group having 1 to 5 carbon atoms. Among these, HFP is preferred.

The copolymer is preferably at least one selected from the group consisting of a copolymer consisting only of the TFE unit and the FAVE unit, and TFE/HFP/FAVE copolymer, and is more preferably a copolymer consisting only of the TFE unit and the FAVE unit.

The melt flow rate (MFR) of the copolymer is 11.0 to 19.0 g/10 min. The MFR of the copolymer is preferably 12.0 g/10 min or higher, and more preferably 13.0 g/10 min or higher, and preferably 18.0 g/10 min or lower, and more preferably 17.6 g/10 min or lower. The injection molded article of the present disclosure can be easily produced by injection molding due to containing a copolymer having a relatively high MFR, and furthermore, is excellent in the ozone resistance, while containing the copolymer having such a relatively high MFR copolymer. When the MFR of the copolymer is too high, the ozone resistance, the abrasion resistance at 150° C., the transparency and the heat distortion resistance after chemical immersion of the injection molded article deteriorate. When the MFR of the copolymer is too low, forming of the copolymer is not easy, and a problem occurs such as, for example, difficulty in preparing an injection molded article having a hollow with a smooth surface and a cross section close to a round. When the MFR of the copolymer is too low, the chemical solution low permeability, the transparency and the swelling resistance to chemical solutions of the injection molded article deteriorate.

In the present disclosure, the MFR is a value obtained as a mass (g/10 min) of the polymer flowing out from a nozzle of 2.1 mm in inner diameter and 8 mm in length per 10 min at 372° C. under a load of 5 kg using a melt indexer, according to ASTM D1238.

The MFR can be regulated by regulating the kind and amount of a polymerization initiator to be used in polymerization of monomers, the kind and amount of a chain transfer agent, and the like.

In the present disclosure, the number of functional groups per 10⁶ main-chain carbon atoms of the copolymer is preferably 20 or less, more preferably 15 or less, and still more preferably less than 6. Due to that the number of functional groups of the copolymer is in the above range, the amount of fluorine ions dissolving out from the injection molded article into water can further easily be reduced, and as a result, not only the ozone resistance of the injection molded article can easily be improved, but also the chemical solution low permeability and the swelling resistance to chemical solutions can be improved.

For identification of the kind of the functional groups and measurement of the number of the functional groups, infrared spectroscopy can be used.

The number of the functional groups is measured, specifically, by the following method. First, the copolymer is formed by cold press to prepare a film of 0.25 to 0.30 mm in thickness. The film is analyzed by Fourier transform infrared spectroscopy to obtain an infrared absorption spectrum of the copolymer, and a difference spectrum against a base spectrum that is completely fluorinated and has no functional groups is obtained. From an absorption peak of a specific functional group observed on this difference spectrum, the number N of the functional group per 1×10⁶ carbon atoms in the copolymer is calculated according to the following formula (A).

N=I×K/t  (A)

-   -   I: absorbance     -   K: correction factor     -   t: thickness of film (mm)

For reference, for some functional groups, the absorption frequency, the molar absorption coefficient and the correction factor are shown in Table 1. Then, the molar absorption coefficients are those determined from FT-IR measurement data of low molecular model compounds.

TABLE 1 Molar Absorption Extinction Functional Frequency Coefficient Correction Group (cm⁻¹) (l/cm/mol) Factor Model Compound —COF 1883 600 388 C₇F₁₅COF —COOH 1815 530 439 H(CF₂)₆COOH free —COOH 1779 530 439 H(CF₂)₆COOH bonded —COOCH₃ 1795 680 342 C₇F₁₅COOCH₃ —CONH₂ 3436 506 460 C₇H₁₅CONH₂ —CH₂OH₂, 3648 104 2236 C₇H₁₅CH₂OH —OH —CF₂H 3020 8.8 26485 H(CF₂CF₂)₃CH₂OH —CF═CF₂ 1795 635 366 CF₂═CF₂

Absorption frequencies of —CH₂CF₂H, —CH₂COF, —CH₂COOH, —CH₂COOCH₃ and —CH₂CONH₂ are lower by a few tens of kaysers (cm⁻¹) than those of —CF₂H, —COF, —COOH free and —COOH bonded, —COOCH₃ and —CONH₂ shown in the Table, respectively.

For example, the number of the functional group —COF is the total of the number of a functional group determined from an absorption peak having an absorption frequency of 1,883 cm⁻¹ derived from —CF₂COF and the number of a functional group determined from an absorption peak having an absorption frequency of 1,840 cm⁻¹ derived from —CH₂COF.

The functional groups are ones present on main chain terminals or side chain terminals of the copolymer, and ones present in the main chain or the side chains. The number of the functional groups may be the total of numbers of —CF═CF₂, —CF₂H, —COF, —COOH, —COOCH₃, —CONH₂ and —CH₂OH.

The functional groups are introduced to the copolymer by, for example, a chain transfer agent or a polymerization initiator used for production of the copolymer. For example, in the case of using an alcohol as the chain transfer agent, or a peroxide having a structure of —CH₂ OH as the polymerization initiator, —CH₂OH is introduced on the main chain terminals of the copolymer. Alternatively, the functional group is introduced on the side chain terminal of the copolymer by polymerizing a monomer having the functional group.

The copolymer satisfying the above range regarding the number of functional groups can be obtained by subjecting the copolymer to a fluorination treatment. That is, the copolymer contained in the injection molded article of the present disclosure is preferably one which is subjected to the fluorination treatment. Further, the copolymer contained in the injection molded article of the present disclosure preferably has —CF₃ terminal groups.

The melting point of the copolymer is preferably 296 to 305° C. and more preferably 299° C. or higher. Due to that the melting point is in the above range, physical properties such as the transparency, the rigidity on heating, the long-time tensile creep property, the deterioration resistance to repeated loads, the abrasion resistance at 150° C., the chemical solution low permeability, the heat distortion resistance after chemical immersion, and the swelling resistance to chemical solutions of the injection molded article are further excellent, and the ozone resistance is further improved.

The injection molded article of the present disclosure may contain other components such as fillers, plasticizers, processing aids, mold release agents, pigments, flame retarders, lubricants, light stabilizers, weathering stabilizers, electrically conductive agents, antistatic agents, ultraviolet absorbents, antioxidants, foaming agents, perfumes, oils, softening agents and dehydrofluorination agents.

Examples of the fillers include silica, kaolin, clay, organo clay, talc, mica, alumina, calcium carbonate, calcium terephthalate, titanium oxide, calcium phosphate, calcium fluoride, lithium fluoride, crosslinked polystyrene, potassium titanate, carbon, boron nitride, carbon nanotube and glass fiber. The electrically conductive agents include carbon black. The plasticizers include dioctyl phthalate and pentaerythritol. The processing aids include carnauba wax, sulfone compounds, low molecular weight polyethylene and fluorine-based auxiliary agents. The dehydrofluorination agents include organic oniums and amidines.

As the above-mentioned other components, other polymers other than the copolymer may be used. The other polymers include fluororesins other than the copolymer, fluoroelastomer, and non-fluorinated polymers.

The copolymer contained in the injection molded article of the present disclosure can be produced by a polymerization method such as suspension polymerization, solution polymerization, emulsion polymerization or bulk polymerization. The polymerization method is preferably emulsion polymerization or suspension polymerization. In these polymerization methods, conditions such as temperature and pressure, and a polymerization initiator and other additives can suitably be set depending on the formulation and the amount of the copolymer.

As the polymerization initiator, an oil-soluble radical polymerization initiator, or a water-soluble radical polymerization initiator may be used.

The oil-soluble radical polymerization initiator may be a known oil-soluble peroxide, and examples thereof typically include:

-   -   dialkyl peroxycarbonates such as di-n-propyl peroxydicarbonate,         diisopropyl peroxydicarbonate, di-sec-butyl peroxydicarbonate         and di-2-ethoxyethyl peroxydicarbonate;     -   peroxyesters such as t-butyl peroxyisobutyrate and t-butyl         peroxypivalate;     -   dialkyl peroxides such as di-t-butyl peroxide; and     -   di[fluoro(or fluorochloro)acyl] peroxides.

The di[fluoro(or fluorochloro)acyl] peroxides include diacyl peroxides represented by [(RfCOO)—]₂ wherein Rf is a perfluoroalkyl group, an ω-hydroperfluoroalkyl group or a fluorochloroalkyl group.

Examples of the di[fluoro(or fluorochloro)acyl] peroxides include di(ω-hydro-dodecafluorohexanoyl) peroxide, di(ω-hydro-tetradecafluoroheptanoyl) peroxide, di(ω-hydrohexadecafluorononanoyl) peroxide, di(perfluoropropionyl) peroxide, di(perfluorobutyryl) peroxide, di(perfluorovaleryl) peroxide, di(perfluorohexanoyl) peroxide, di(perfluoroheptanoyl) peroxide, di(perfluorooctanoyl) peroxide, di(perfluorononanoyl) peroxide, di(ω-chloro-hexafluorobutyryl) peroxide, di(ω-chloro-decafluorohexanoyl) peroxide, di(ω-chloro-tetradecafluorooctanoyl) peroxide, ω-hydrodo-decafluoroheptanoyl-ω-hydrohexadecafluorononanoyl peroxide, co-chloro-hexafluorobutyryl-ω-chloro-decafluorohexanoyl peroxide, ω-hydrododecafluoroheptanoyl-perfluorobutyryl peroxide, di(dichloropentafluorobutanoyl) peroxide, di(trichlorooctafluorohexanoyl) peroxide, di(tetrachloroundecafluorooctanoyl) peroxide, di(pentachlorotetradecafluorodecanoyl) peroxide and di(undecachlorotriacontafluorodocosanoyl) peroxide.

The water-soluble radical polymerization initiator may be a known water-soluble peroxide, and examples thereof include ammonium salts, potassium salts and sodium salts of persulfuric acid, perboric acid, perchloric acid, perphosphoric acid, percarbonic acid and the like, organic peroxides such as disuccinoyl peroxide and diglutaroyl peroxide, and t-butyl permaleate and t-butyl hydroperoxide. A reductant such as a sulfite salt may be combined with a peroxide and used, and the amount thereof to be used may be 0.1 to 20 times with respect to the peroxide.

In the polymerization, a surfactant, a chain transfer agent and a solvent may be used, which are conventionally known. The surfactant may be a known surfactant, for example, nonionic surfactants, anionic surfactants and cationic surfactants may be used. Among these, fluorine-containing anionic surfactants are preferred, and more preferred are linear or branched fluorine-containing anionic surfactants having 4 to 20 carbon atoms, which may contain an ether bond oxygen (that is, an oxygen atom may be inserted between carbon atoms). The amount of the surfactant to be added (with respect to water in the polymerization) is preferably 50 to 5,000 ppm.

Examples of the chain transfer agent include hydrocarbons such as ethane, isopentane, n-hexane and cyclohexane; aromatics such as toluene and xylene; ketones such as acetone; acetate esters such as ethyl acetate and butyl acetate; alcohols such as methanol and ethanol; mercaptans such as methylmercaptan; and halogenated hydrocarbons such as carbon tetrachloride, chloroform, methylene chloride and methyl chloride. The amount of the chain transfer agent to be added may vary depending on the chain transfer constant value of the compound to be used, but is usually in the range of 0.01 to 20% by mass with respect to the solvent in the polymerization.

The solvent may include water and mixed solvents of water and an alcohol.

In the suspension polymerization, in addition to water, a fluorosolvent may be used. The fluorosolvent may include hydrochlorofluoroalkanes such as CH₃CClF₂, CH₃CCl₂F, CF₃CF₂CCl₂H and CF₂ClCF₂CFHCl; chlorofluoroalaknes such as CF₂ClCFClCF₂CF₃ and CF₃CFClCFClCF₃; hydrofluroalkanes such as CF₃CFHCFHCF₂CF₂CF₃, CF₂HCF₂CF₂CF₂CF₂H and CF₃CF₂CF₂CF₂CF₂CF₂CF₂H; hydrofluoroethers such as CH₃OC₂F₅, CH₃OC₃F₅CF₃CF₂CH₂OCHF₂, CF₃CHFCF₂OCH₃, CHF₂CF₂OCH₂F, (CF₃)₂CHCF₂OCH₃, CF₃CF₂CH₂OCH₂CHF₂ and CF₃CHFCF₂OCH₂CF₃; and perfluoroalkanes such as perfluorocyclobutane, CF₃CF₂CF₂CF₃, CF₃CF₂CF₂CF₂CF₃ and CF₃CF₂CF₂CF₂CF₂CF₃, and among these, perfluoroalkanes are preferred. The amount of the fluorosolvent to be used is, from the viewpoint of the suspensibility and the economic efficiency, preferably 10 to 100% by mass with respect to an aqueous medium.

The polymerization temperature is not limited, and may be 0 to 100° C. The polymerization pressure is suitably set depending on other polymerization conditions to be used such as the kind, the amount and the vapor pressure of the solvent, and the polymerization temperature, but may usually be 0 to 9.8 MPaG.

In the case of obtaining an aqueous dispersion containing the copolymer by the polymerization reaction, the copolymer can be recovered by coagulating, cleaning and drying the copolymer contained in the aqueous dispersion. Then in the case of obtaining the copolymer as a slurry by the polymerization reaction, the copolymer can be recovered by taking out the slurry from a reaction container, and cleaning and drying the slurry. The copolymer can be recovered in a shape of powder by the drying.

The copolymer obtained by the polymerization may be formed into pellets. A method of forming into pellets is not limited, and a conventionally known method can be used. Examples thereof include methods of melt extruding the copolymer by using a single-screw extruder, a twin-screw extruder or a tandem extruder and cutting the resultant into a predetermined length to form the copolymer into pellets. The extrusion temperature in the melt extrusion needs to be varied depending on the melt viscosity and the production method of the copolymer, and is preferably the melting point of the copolymer+20° C. to the melting point of the copolymer+140° C. A method of cutting the copolymer is not limited, and there can be adopted a conventionally known method such as a strand cut method, a hot cut method, an underwater cut method, or a sheet cut method. Volatile components in the obtained pellets may be removed by heating the pellets (degassing treatment). Alternatively, the obtained pellets may be treated by bringing the pellets into contact with hot water of 30 to 200° C., steam of 100 to 200° C. or hot air of 40 to 200° C.

Alternatively, the copolymer obtained by the polymerization may be subjected to fluorination treatment. The fluorination treatment can be carried out by bringing the copolymer having been subjected to no fluorination treatment into contact with a fluorine-containing compound. By the fluorination treatment, thermally unstable functional groups of the copolymer, such as —COOH, —COOCH₃, —CH₂OH, —COF, —CF═CF₂ and —CONH₂, and thermally relatively stable functional groups thereof, such as —CF₂H, can be converted to thermally very stable —CF₃. Consequently, the total number (number of functional groups) of —COOH, —COOCH₃, —CH₂OH, —COF, —CF═CF₂, —CONH₂ and —CF₂H of the copolymer can easily be controlled in the above-mentioned range.

The fluorine-containing compound is not limited, but includes fluorine radical sources generating fluorine radicals under the fluorination treatment condition. The fluorine radical sources include F₂ gas, CoF₃, AgF₂, UF₆, OF₂, N₂F₂, CF₃OF, halogen fluorides (for example, IF₅ and ClF₃).

The fluorine radical source such as F₂ gas may be, for example, one having a concentration of 100%, but from the viewpoint of safety, the fluorine radical source is preferably mixed with an inert gas and diluted therewith to 5 to 50% by mass, and then used; and it is more preferably to be diluted to 15 to 30% by mass. The inert gas includes nitrogen gas, helium gas and argon gas, but from the viewpoint of the economic efficiency, nitrogen gas is preferred.

The condition of the fluorination treatment is not limited, and the copolymer in a melted state may be brought into contact with the fluorine-containing compound, but the fluorination treatment can be carried out usually at a temperature of not higher than the melting point of the copolymer, preferably at 20 to 240° C. and more preferably at 100 to 220° C. The fluorination treatment is carried out usually for 1 to 30 hours and preferably 5 to 25 hours. The fluorination treatment is preferred which brings the copolymer having been subjected to no fluorination treatment into contact with fluorine gas (F₂ gas).

In the method for producing the copolymer contained in the injection molded article of the present disclosure, it is preferable to use the production method described in Japanese Patent Laid-Open No. 2020-97750.

In the method for producing the copolymer contained in the injection molded article of the present disclosure, it is preferable not to bring the material and copolymer to be used in the production into contact with the metal surface of each facility and piping in each step for producing the copolymer that is subjected to injection molding, such as a polymerization step, a granulation step, a cleaning step, a drying step, a transfer step, a storing step, a pelletization step, a fluorination step, and a product filling step, and it is also preferable to use a material having a low metal content as the material to be used in the production. By such a method, an injection molded article in which the amount of metal dissolving out into 50% by mass hydrofluoric acid is eventually further reduced can easily be obtained.

In the method for producing the copolymer contained in the injection molded article of the present disclosure, it is preferable to use clean and dry air as the air to be used to dry the copolymer and the air to be used in the transfer of the copolymer in each facility. By such a method, an injection molded article in which the amount of metal dissolving out into 50% by mass hydrofluoric acid is eventually further reduced can easily be obtained.

By producing the copolymer as above, a copolymer having, for example, a metal content measured by the ash method of 100 ng/1 g or lower can be obtained. Due to that the injection molded article in which the amount of metal dissolving out into 50% by mass hydrofluoric acid is further reduced can easily be obtained, the metal content of the copolymer subjected to injection molding is preferably 100 ng/1 g or lower, more preferably 60 ng/1 g or lower, still more preferably 50 ng/1 g or lower, especially preferably 40 ng/1 g or lower, and most preferably 30 ng/1 g or lower; and the lower limit is not limited, but may be 1 ng/1 g or higher.

As the method for measuring the metal content in the copolymer, there can be used a method in which the copolymer is ashed in a cuvette in the atomization part of atomic absorption spectrophotometer and the metal content is measured using the atomic absorption spectrophotometer, a method in which the copolymer is weighed in a platinum crucible and ashed using a gas burner or an electric furnace, the ash is dissolved out in acid, and then the metal content is measured using an ICP emission analyzer or a flameless atomic absorption spectrophotometer, or the like.

By injection molding the copolymer obtained as above, the injection molded article can be obtained.

In the production method comprising injection molding a copolymer using an injection molding machine provided with a cylinder and a screw accommodated in the cylinder to obtain an injection molded article, the injection molded article of the present disclosure can suitably be produced by using a copolymer which has a content of the PAVE unit, an MFR and a melting point within the above-mentioned ranges, and has the number of functional groups per 10⁶ main-chain carbon atoms of 20 or less, and preferably 15 or less.

The production method of the present disclosure, due to having the above configuration, enables an injection molded article in which the amount of fluorine ions dissolving out into water is reduced to be easily obtained, and furthermore, enables an injection molded article in a complicated shape to be easily produced, and for example, enables an injection molded article such as a female joint to be easily produced.

In the production method of the present disclosure, an injection molded article in which the amount of fluorine ions dissolving out into water is further reduced can be obtained by adjusting the temperature of the cylinder to 385 to 395° C. The cylinder temperature is preferably 392° C. or lower, and is more preferably 390° C. or lower.

In the production method of the present disclosure, an injection molded article in which the amount of metal dissolving out into 50% by mass hydrofluoric acid is reduced can be obtained by using a Ni plated cylinder or a cylinder formed of a Ni-based alloy as the cylinder and a screw formed of a Ni-based alloy and provided with a smear head on a head end as the screw.

The shape of the copolymer to be supplied into an injection molding machine is not limited, and a copolymer in a shape of powder, pellet, or the like can be used.

A known injection molding machine can be used. The copolymer injected from a nozzle of an injection molding machine usually passes through a sprue, a runner, and a gate, flows into a mold cavity, and is filled in the mold cavity. In the mold used for injection molding, a runner and a gate are formed, and a mold cavity for forming an injection molded article is formed.

The shape of the sprue is not limited, and may be a circle, a rectangle, a trapezoid, or the like. The shape of the runner is not limited, and may be a circle, a rectangle, a trapezoid, or the like. The runner type is not limited, and may be a cold runner or a hot runner. The gate type is not limited, and may be a direct gate, a side gate, a submarine gate, or the like. The number of gates to the mold cavity is not limited. Any of the mold having a single-gate structure and the mold having a multi-gate structure may be used. The number of mold cavities of the mold (number of cavities) is preferably 1 to 64.

The injection molded article of the present disclosure can be used in various applications. The injection molded article of the present disclosure may be, for example, nuts, bolts, joints, female joints, films, bottles, gaskets, tubes, hoses, pipes, valves, sheets, seals, packings, tanks, rollers, containers, cocks, connectors, filter housings, filter cages, flowmeters, pumps, wafer carrier, or wafer boxes.

Due to that the injection molded article of the present disclosure is excellent in physical properties such as the transparency, the rigidity on heating, the long-time tensile creep property, the deterioration resistance to repeated loads, the abrasion resistance at 150° C., the chemical solution low permeability, the heat distortion resistance after chemical immersion and the swelling resistance to chemical solutions, and is remarkably excellent in the ozone resistance, the injection molded article can suitably be utilized for nuts, bolts, joints, packings, valves, cocks, connectors, filter housings, filter cages, flowmeters, pumps, and the like. For example, the injection molded article of the present disclosure can suitably be utilized as piping members (in particular, housings of valves and filter cages) to be used in the transfer of chemical solutions, and flowmeter frames provided with flow paths for chemical solutions in flowmeters. The piping member and flowmeter frame of the present disclosure is excellent in physical properties such as the transparency, the rigidity on heating, the long-time tensile creep property, the deterioration resistance to repeated loads, the abrasion resistance at 150° C., the chemical solution low permeability, the heat distortion resistance after chemical immersion and the swelling resistance to chemical solutions, and is also remarkably excellent in the ozone resistance. Hence, the piping member and flowmeter frame of the present disclosure are excellent in the viewability of the inside, and in particular, the flowmeter frame enables the float in the inside to be easily visually observed and observed by a camera or the like, can be suitably used also in the measurement of the flow rate of a chemical solution at about 150° C., and are hardly damaged even when stresses are repeatedly applied according to the start of the flow, the stop of the flow, and the change of the flow of the chemical solution.

The injection molded article of the present disclosure can suitably be utilized as members to be compressed, such as gaskets and packings which are excellent in physical properties such as the transparency, the rigidity on heating, the long-time tensile creep property, the deterioration resistance to repeated loads, the abrasion resistance at 150° C., the chemical solution low permeability, the heat distortion resistance after chemical immersion and the swelling resistance to chemical solutions, and are also remarkably excellent in the ozone resistance.

The injection molded article of the present disclosure can suitably be utilized as bottles or tubes which are excellent in physical properties such as the transparency, the rigidity on heating, the long-time tensile creep property, the deterioration resistance to repeated loads, the abrasion resistance at 150° C., the chemical solution low permeability, the heat distortion resistance after chemical immersion and the swelling resistance to chemical solutions, and are also remarkably excellent in the ozone resistance. The bottles or tubes of the present disclosure enable the content to be easily visually recognized and are hardly damaged during use.

The injection molded article of the present disclosure is excellent in physical properties such as the transparency, the rigidity on heating, the long-time tensile creep property, the deterioration resistance to repeated loads, the abrasion resistance at 150° C., the chemical solution low permeability, the heat distortion resistance after chemical immersion and the swelling resistance to chemical solutions, and is also remarkably excellent in the ozone resistance. Therefore, the injection molded article of the present disclosure can suitably be utilized for housings of valves and valves. The valves of the present disclosure are excellent in physical properties such as the transparency, the rigidity on heating, the long-time tensile creep property, the deterioration resistance to repeated loads, the abrasion resistance at 150° C., the chemical solution low permeability, the heat distortion resistance after chemical immersion and the swelling resistance to chemical solutions, and are also excellent in the ozone resistance.

Although the embodiments have been described above, it will be understood that various changes in form and details are possible without departing from the gist and scope of the claims.

According to the present disclosure, there is provided an injection molded article comprising a copolymer comprising tetrafluoroethylene unit and a fluoro(alkyl vinyl ether) unit, wherein the content of the fluoro(alkyl vinyl ether) unit of the copolymer is 3.9 to 4.8% by mass with respect to the whole of the monomer units, the melt flow rate at 372° C. of the copolymer is 11.0 to 19.0 g/10 min, the melting point of the copolymer is 296 to 305° C., and the amount of fluorine ions dissolving out from the injection molded article into water is 7,500 μg/m² or lower.

In the injection molded article of the present disclosure, the amount of fluorine ions dissolving out from the injection molded article into water is preferably 5,500 μg/m² or lower.

In the injection molded article of the present disclosure, the amount of metal dissolving out from the injection molded article into 50% by mass hydrofluoric acid is preferably 200 μg/m² or lower.

In the injection molded article of the present disclosure, the fluoro(alkyl vinyl ether) unit of the copolymer is preferably a perfluoro(propyl vinyl ether) unit.

In the injection molded article of the present disclosure, the content of the fluoro(alkyl vinyl ether) unit of the copolymer is preferably 4.1 to 4.5% by mass with respect to the whole of the monomer units.

In the injection molded article of the present disclosure, the melt flow rate at 372° C. of the copolymer is preferably 12.0 to 17.6 g/10 min.

In the injection molded article of the present disclosure, the number of functional groups of the copolymer is preferably 20 or less per 10⁶ main-chain carbon atoms.

The injection molded article of the present disclosure is preferably a female joint.

According to the present disclosure, there is provided a method for producing the above injection molded article, comprising injection molding the copolymer using an injection molding machine provided with a cylinder and a screw accommodated in the cylinder, to obtain the injection molded article.

In the production method of the present disclosure, the temperature of the copolymer in the cylinder is preferably adjusted to 385 to 395° C.

In the production method of the present disclosure, a Ni plated cylinder or a cylinder formed of a Ni-based alloy is preferably used as the cylinder, and a screw formed of a Ni-based alloy and provided with a smear head on a head end is preferably used as the screw.

EXAMPLES

Next, embodiments of the present disclosure will be described with reference to experimental examples, but the present disclosure is not intended to be limited by these experimental examples.

The numerical values of the experimental examples were measured by the following methods.

(Content of a Monomer Unit)

The content of each monomer unit was measured by an NMR analyzer (for example, manufactured by Bruker BioSpin GmbH, AVANCE 300, high-temperature probe).

(Melt Flow Rate (MFR))

The polymer was made to flow out from a nozzle of 2.1 mm in inner diameter and 8 mm in length at 372° C. under a load of 5 kg by using a Melt Indexer G-01 (manufactured by Toyo Seiki Seisaku-sho, Ltd.) according to ASTM D1238, and the mass (g/10 min) of the polymer flowing out per 10 min was determined.

(Melting Point)

The polymer was heated, as a first temperature raising step at a temperature-increasing rate of 10° C./min from 200° C. to 350° C., then cooled at a cooling rate of 10° C./min from 350° C. to 200° C., and then again heated, as second temperature raising step, at a temperature-increasing rate of 10° C./min from 200° C. to 350° C. by using a differential scanning calorimeter (trade name: X-DSC7000, manufactured by Hitachi High-Tech Science Corp.); and the melting point was determined from a melting curve peak observed in the second temperature raising step.

(Number of Functional Groups)

Pellets of the copolymer was formed by cold press into a film of 0.25 to 0.30 mm in thickness. The film was 40 times scanned and analyzed by a Fourier transform infrared spectrometer [FT-IR (Spectrum One, manufactured by PerkinElmer, Inc.)] to obtain an infrared absorption spectrum, and a difference spectrum against a base spectrum that is completely fluorinated and has no functional groups is obtained. From an absorption peak of a specific functional group observed on this difference spectrum, the number N of the functional group per 1×10⁶ carbon atoms in the sample was calculated according to the following formula (A).

N=I×K/t  (A)

-   -   I: absorbance     -   K: correction factor     -   t: thickness of film (mm)

Regarding the functional groups in the present disclosure, for reference, the absorption frequency, the molar absorption coefficient and the correction factor are shown in Table 2. The molar absorption coefficients are those determined from FT-IR measurement data of low molecular model compounds.

TABLE 2 Molar Absorption Extinction Functional Frequency Coefficient Correction Group (cm⁻¹) (l/cm/mol) Factor Model Compound —COF 1883 600 388 C₇F₁₅COF —COOH free 1815 530 439 H(CF₂)₆COOH —COOH 1779 530 439 H(CF₂)₆COOH bonded —COOCH₃ 1795 680 342 C₇F₁₅COOCH₃ —CONH₂ 3436 506 460 C₇H₁₅CONH₂ —CH₂OH₂, 3648 104 2236 C₇H₁₅CH₂OH —OH —CF₂H 3020  8.8 26485 H(CF₂CF₂)₃CH₂OH —CF═CF₂ 1795 635 366 CF₂═CF₂

Synthesis Example 1

Pellets were obtained in the same manner as described in Example 1 of Japanese Patent Laid-Open No. 2020-97750, except for changing the charged amount of pure water to 51.8 L, changing the charged amount of perfluorocyclobutane to 40.9 kg, changing the charged amount of perfluoro(propyl vinyl ether) (PPVE) to 1.57 kg, changing the charged amount of methanol to 1.03 kg, introducing tetrafluoroethylene (TFE) under pressure up to 0.64 MPa, charging 0.103 kg of a 50% methanol solution of di-n-propyl peroxydicarbonate instead of di-sec-butyl peroxydicarbonate, adding 0.038 kg of PPVE for every 1 kg of TFE supplied, finishing the polymerization at the time when the amount of TFE additionally charged reached 40.9 kg, to thereby obtain 42.4 kg of a dry powder. By using the obtained pellets, the PPVE content was measured by the above-mentioned method. The results are shown in Table 3.

The obtained pellets were put in a vacuum vibration-type reactor VVD-30 (manufactured by Okawara MFG. Co., Ltd.), and heated to 210° C. After vacuumizing, F₂ gas diluted to 20% by volume with N₂ gas was introduced to the atmospheric pressure. 0.5 hour after the F₂ gas introduction, vacuumizing was once carried out and the F₂ gas was again introduced. Further, 0.5 hour thereafter, vacuumizing was again carried out and F₂ gas was again introduced. Thereafter, while the above operation of the F₂ gas introduction and the vacuumizing was carried out once every 1 hour, the reaction was carried out at a temperature of 210° C. for 10 hours. After the reaction was finished, the reactor interior was replaced sufficiently by N₂ gas to finish the fluorination reaction. By using the fluorinated pellets, the above physical properties were measured by the methods described above. The results are shown in Table 3.

Synthesis Example 2

Pellets were obtained in the same manner as described in Example 1 of Japanese Patent Laid-Open No. 2020-97750, except for changing the charged amount of pure water to 51.8 L, changing the charged amount of perfluorocyclobutane to 40.9 kg, changing the charged amount of perfluoro(propyl vinyl ether) (PPVE) to 2.69 kg, changing the charged amount of methanol to 2.48 kg, introducing tetrafluoroethylene (TFE) under pressure up to 0.64 MPa, charging 0.051 kg of a 50% methanol solution of di-n-propyl peroxydicarbonate instead of di-sec-butyl peroxydicarbonate, adding 0.057 kg of PPVE for every 1 kg of TFE supplied, finishing the polymerization at the time when the amount of TFE additionally charged reached 40.9 kg, to thereby obtain 43.2 kg of a dry powder. By using the obtained pellets, the PPVE content was measured by the above-mentioned method. The results are shown in Table 3.

Fluorinated pellets were obtained as in Synthesis Example 1, except for using the obtained pellets. The results are shown in Table 3.

Synthesis Example 3

Pellets were obtained in the same manner as described in Example 1 of Japanese Patent Laid-Open No. 2020-97750, except for changing the charged amount of pure water to 51.8 L, changing the charged amount of perfluorocyclobutane to 40.9 kg, changing the charged amount of perfluoro(propyl vinyl ether) (PPVE) to 1.92 kg, changing the charged amount of methanol to 3.09 kg, introducing tetrafluoroethylene (TFE) under pressure up to 0.64 MPa, charging 0.051 kg of a 50% methanol solution of di-n-propyl peroxydicarbonate instead of di-sec-butyl peroxydicarbonate, adding 0.044 kg of PPVE for every 1 kg of TFE supplied, finishing the polymerization at the time when the amount of TFE additionally charged reached 40.9 kg, to thereby obtain 42.7 kg of a dry powder. By using the obtained pellets, the PPVE content was measured by the above-mentioned method. The results are shown in Table 3.

Fluorinated pellets were obtained as in Synthesis Example 1, except for using the obtained pellets. The results are shown in Table 3.

Synthesis Example 4

Pellets were obtained in the same manner as described in Example 1 of Japanese Patent Laid-Open No. 2020-97750, except for changing the charged amount of pure water to 51.8 L, changing the charged amount of perfluorocyclobutane to 40.9 kg, changing the charged amount of perfluoro(propyl vinyl ether) (PPVE) to 2.05 kg, changing the charged amount of methanol to 4.13 kg, introducing tetrafluoroethylene (TFE) under pressure up to 0.64 MPa, charging 0.051 kg of a 50% methanol solution of di-n-propyl peroxydicarbonate instead of di-sec-butyl peroxydicarbonate, adding 0.046 kg of PPVE for every 1 kg of TFE supplied, finishing the polymerization at the time when the amount of TFE additionally charged reached 40.9 kg, to thereby obtain 42.8 kg of a dry powder. By using the obtained pellets, the PPVE content was measured by the above-mentioned method. The results are shown in Table 3.

Fluorinated pellets were obtained as in Synthesis Example 1, except for using the obtained pellets, changing the raised temperature of the vacuum vibration-type reactor to 160° C., and changing the reaction condition to at 160° C. and for 5 hours. The results are shown in Table 3.

Synthesis Example 5

Pellets were obtained in the same manner as described in Example 1 of Japanese Patent Laid-Open No. 2020-97750, except for changing the charged amount of pure water to 51.8 L, changing the charged amount of perfluorocyclobutane to 40.9 kg, changing the charged amount of perfluoro(propyl vinyl ether) (PPVE) to 1.85 kg, changing the charged amount of methanol to 4.00 kg, introducing tetrafluoroethylene (TFE) under pressure up to 0.64 MPa, charging 0.051 kg of a 50% methanol solution of di-n-propyl peroxydicarbonate instead of di-sec-butyl peroxydicarbonate, adding 0.043 kg of PPVE for every 1 kg of TFE supplied, finishing the polymerization at the time when the amount of TFE additionally charged reached 40.9 kg, to thereby obtain 42.6 kg of a dry powder. By using the obtained pellets, the PPVE content was measured by the above-mentioned method. The results are shown in Table 3.

Fluorinated pellets were obtained as in Synthesis Example 1, except for using the obtained pellets. The results are shown in Table 3.

Synthesis Example 6

Pellets were obtained in the same manner as described in Example 1 of Japanese Patent Laid-Open No. 2020-97750, except for changing the charged amount of pure water to 51.8 L, changing the charged amount of perfluorocyclobutane to 40.9 kg, changing the charged amount of perfluoro(propyl vinyl ether) (PPVE) to 1.92 kg, changing the charged amount of methanol to 4.17 kg, introducing tetrafluoroethylene (TFE) under pressure up to 0.64 MPa, charging 0.051 kg of a 50% methanol solution of di-n-propyl peroxydicarbonate instead of di-sec-butyl peroxydicarbonate, adding 0.044 kg of PPVE for every 1 kg of TFE supplied, finishing the polymerization at the time when the amount of TFE additionally charged reached 40.9 kg, to thereby obtain 42.7 kg of a dry powder. By using the obtained pellets, the PPVE content was measured by the above-mentioned method. The results are shown in Table 3.

Fluorinated pellets were obtained as in Synthesis Example 1, except for using the obtained pellets. The results are shown in Table 3.

Synthesis Example 7

Pellets were obtained in the same manner as described in Example 1 of Japanese Patent Laid-Open No. 2020-97750, except for changing the charged amount of pure water to 51.8 L, changing the charged amount of perfluorocyclobutane to 40.9 kg, changing the charged amount of perfluoro(propyl vinyl ether) (PPVE) to 1.98 kg, changing the charged amount of methanol to 4.37 kg, introducing tetrafluoroethylene (TFE) under pressure up to 0.64 MPa, charging 0.051 kg of a 50% methanol solution of di-n-propyl peroxydicarbonate instead of di-sec-butyl peroxydicarbonate, adding 0.045 kg of PPVE for every 1 kg of TFE supplied, finishing the polymerization at the time when the amount of TFE additionally charged reached 40.9 kg, to thereby obtain 42.7 kg of a dry powder. By using the obtained pellets, the PPVE content was measured by the above-mentioned method. The results are shown in Table 3.

Fluorinated pellets were obtained as in Synthesis Example 1, except for using the obtained pellets. The results are shown in Table 3.

Synthesis Example 8

Pellets were obtained in the same manner as described in Example 1 of Japanese Patent Laid-Open No. 2020-97750, except for changing the charged amount of pure water to 51.8 L, changing the charged amount of perfluorocyclobutane to 40.9 kg, changing the charged amount of perfluoro(propyl vinyl ether) (PPVE) to 2.11 kg, changing the charged amount of methanol to 0.16 kg, introducing tetrafluoroethylene (TFE) under pressure up to 0.64 MPa, charging 0.103 kg of a 50% methanol solution of di-n-propyl peroxydicarbonate instead of di-sec-butyl peroxydicarbonate, adding 0.047 kg of PPVE for every 1 kg of TFE supplied, finishing the polymerization at the time when the amount of TFE additionally charged reached 40.9 kg, to thereby obtain 42.8 kg of a dry powder. By using the obtained pellets, the PPVE content was measured by the above-mentioned method. The results are shown in Table 3.

Fluorinated pellets were obtained as in Synthesis Example 1, except for using the obtained pellets. The results are shown in Table 3.

Synthesis Example 9

Pellets were obtained in the same manner as described in Example 1 of Japanese Patent Laid-Open No. 2020-97750, except for changing the charged amount of pure water to 51.8 L, changing the charged amount of perfluorocyclobutane to 40.9 kg, changing the charged amount of perfluoro(propyl vinyl ether) (PPVE) to 2.11 kg, changing the charged amount of methanol to 1.12 kg, introducing tetrafluoroethylene (TFE) under pressure up to 0.64 MPa, charging 0.103 kg of a 50% methanol solution of di-n-propyl peroxydicarbonate instead of di-sec-butyl peroxydicarbonate, adding 0.047 kg of PPVE for every 1 kg of TFE supplied, finishing the polymerization at the time when the amount of TFE additionally charged reached 40.9 kg, to thereby obtain 42.8 kg of a dry powder. By using the obtained pellets, the PPVE content was measured by the above-mentioned method. The results are shown in Table 3.

Fluorinated pellets were obtained as in Synthesis Example 1, except for using the obtained pellets. The results are shown in Table 3.

TABLE 3 Number of PPVE Melting functional content MFR point groups (% by mass) (g/10 min) (° C.) (number/C10⁶) Synthesis 3.6 15.0 307 <6 Example 1 Synthesis 5.4 15.0 302 <6 Example 2 Synthesis 4.2 10.0 303 <6 Example 3 Synthesis 4.4 14.6 304 46 Example 4 Synthesis 4.1 12.0 304 <6 Example 5 Synthesis 4.2 13.5 304 <6 Example 6 Synthesis 4.3 15.0 304 <6 Example 7 Synthesis 4.5 17.6 304 <6 Example 8 Synthesis 4.5 23.0 304 <6 Example 9

The description of “<6” in Table 3 means that the number of functional groups is less than 6.

Experimental Examples 1 to 4 and 6 and Comparative Examples 1 to 5

Forming was carried out in a clean room of class 10000 using an injection molding machine (SE50EV-A, manufactured by Sumitomo Heavy Industries, Ltd.). As the screw of the injection molding machine, a screw in which a smear head is provided on a screw head was used, and the material of the screw and the cylinder of the injection molding machine was a Ni-based alloy. By setting the maximum temperature of the cylinder of the injection molding machine as described in Table 4 and setting the mold temperature to 200° C. and the injection speed to 20 mm/s, the copolymer was injection molded to prepare a sheet-shape injection molded article (40 mm×40 mm×0.5 mmt). The mold used was a mold (4 cavities of 40 cm×40 cm×0.5 mmt, side gate) Ni plated on HPM38.

Injection molding of the copolymer was repeated 100 times, the molding machine and the heater were stopped, and after 22 hours, the molding machine was operated again, and injection molding of the polymer was repeated further 100 times.

Experimental Example 5

Forming was carried out by using an injection molding machine (manufactured by Sumitomo Heavy Industries, Ltd., SE50EV-A). As the screw of the injection molding machine, a screw in which a screw head end configured from a screw head, a non-return ring and a seal ring (three-piece set) is provided was used, and the material of the screw and the cylinder of the injection molding machine was stainless, on which surface Cr was plated. By setting the maximum temperature of the cylinder of the injection molding machine as described in Table 4 and setting the mold temperature to 200° C. and the injection speed to 20 mm/s, the copolymer was injection molded to prepare a sheet-shape injection molded article (40 mm×40 mm×0.5 mmt). The mold used was a mold (4 cavities of 40 mm×40 mm×0.5 mmt, side gate) made of HPM38.

Injection molding of the copolymer was repeated 100 times, the molding machine and the heater were stopped, and after 22 hours, the molding machine was operated again, and injection molding of the polymer was repeated further 100 times.

By using the injection molded articles obtained in Experimental Examples and Comparative Examples, the amount of fluorine ions dissolving out and the amount of metal dissolving out were measured by the following methods. The results are shown in Table 4.

(Measurement of Amount of Fluorine Ions Dissolving Out)

In the measurement of the amount of fluorine ions dissolving out, the injection molded article obtained in the 199th injection molding was used. Four sheet-shape injection molded articles (40 mm×40 mm×0.5 mmt) were cut from the runner of the obtained injection molded article using ceramic scissors. All the four sheet-shape injection molded articles were immersed in 14 g of pure water, heated in a sterilization machine at 121° C. for 1 hour, then the injection molded articles were taken out from the obtained water, and the fluorine ion concentration of the remaining water was measured with a fluorine ion meter. From the obtained measured value, the amount of fluorine ions dissolving out per surface area of the injection molded article was calculated according to the following formula.

Amount of fluorine ions dissolving out (μg/m²)=measured value (μg/g)×amount of pure water (g)/total surface area of four sheet-shape injection molded articles (m²)

(Measurement of Amount of Metal Dissolving Out)

In the measurement of the amount of fluorine ions dissolving out, the injection molded article obtained in the 200th injection molding was used. As the container used in the measurement, a container made of PFA which was immersed in 50% by mass hydrofluoric acid at 25° C. for 7 days, and then washed with ultrapure water was used.

Four sheet-shape injection molded articles (40 mm×40 mm×0.5 mmt) were cut from the runner of the obtained injection molded article using ceramic scissors. All the four sheet-shape injection molded articles were immersed in 50% by mass hydrofluoric acid at 25° C. for 24 hours in the container made of PFA, and then the injection molded articles were taken out. Subsequently, the container made of PFA was installed in a water bath and heated to completely evaporate the moisture from hydrofluoric acid, and then a 0.1 N nitric acid aqueous solution was added to prepare a solution for measurement. At the same time, only hydrofluoric acid was allowed to stand at 25° C. for 24 hours in a container made of PFA, and a solution for reference was prepared in the same manner as above.

Using an ICP emission analyzer (SPECTROBLUE TI, manufactured by SPECTRO Analytical Instruments GmbH), the concentration of iron, chrome, and nickel (metal concentration) in the solution for measurement and the solution for reference was measured. From the obtained measured value, the amount of metal dissolving out per surface area of the injection molded article was calculated according to the following formula.

Amount of metal dissolving out (μg/m²)=[metal concentration in solution for measurement (ng/g)−metal concentration in solution for reference (ng/g)]×amount of 50% by mass hydrofluoric acid (g)×0.001 (μg/ng)/total surface area of four injection molded articles (m²)

Experimental Examples 7 to 10 and Comparative Examples 6 to 10

Forming was carried out in a clean room of class 10000 using an injection molding machine (SE50EV-A, manufactured by Sumitomo Heavy Industries, Ltd.). As the screw of the injection molding machine, a screw in which a smear head is provided on a screw head was used, and the material of the screw and the cylinder of the injection molding machine was a Ni-based alloy. By setting the maximum temperature of the cylinder of the injection molding machine to 390° C., the mold temperature to 200° C. and the injection speed to 10 mm/s, the copolymer was injection molded to prepare a sheet-shape injection molded article (100 mm×100 mm×2 mmt). The mold used was a mold (100 cm×100 cm×2 mmt, side gate) Ni plated on HPM38.

Injection molding of the copolymer was repeated 100 times, the molding machine and the heater were stopped, and after 22 hours, the molding machine was operated again, and injection molding of the polymer was repeated further 100 times.

By using the injection molded articles obtained in Experimental Examples and Comparative Examples, the amount of fluorine ions dissolving out and the amount of metal dissolving out were measured by the method described above. The results are shown in Table 5.

The injection moldability of the copolymers used in Experimental Examples 7 to 10 and Comparative Examples 6 to 10 was evaluated by the following method. The results are shown in Table 5.

(Injection Moldability)

The obtained injection molded article was observed and evaluated according to the following criteria. The presence/absence of roughness of the surface was checked by touching the surface of the injection molded article.

Evaluation (Visually Observed)

-   -   2: The entire surface was flat, and no flow marks were observed         on the entire formed article     -   1: Roughness was observed on the surface within the region of 1         cm from the portion where the gate of the mold had been         positioned, or while a flow mark was observed on the surface         within the region of 1 cm from the portion where the gate of the         mold had been positioned, the entire surface was flat and no         flow marks were observed on other regions     -   0: Roughness was observed on the surface within the region of 4         cm from the portion where the gate of the mold had been         positioned, or a flow mark was observed within the region of 4         cm from the portion where the gate of the mold had been         positioned

The injection molded articles obtained in Experimental Examples and Comparative Examples were evaluated by the following method. The results are shown in Table 4 and Table 5.

(Ozone Exposure Test)

Ozone gas (ozone/oxygen=10/90 capacity %) generated in an ozone generation apparatus (trade name: SGX-A11MN (revised), manufactured by SUMITOMO PRECISION PRODUCTS Co., Ltd.) was connected to a container made of PFA in which ion-exchange water was put, bubbled into the ion-exchange water to add water vapor to the ozone gas, and thereafter, passed through a cell made of PFA in which the sheet-shape injection molded article was put at 0.7 liter/min at room temperature, thereby exposing the sample to wet ozone gas. The sample was taken out 90 days after the start of the exposure, the surface was gently rinsed with ion-exchange water, and thereafter, the portion with a depth of 5 to 200 μm from the sample surface was observed using a transmission type optical microscope at a magnification of ×100 and photographed with a standard scale, and the number of cracks having a length of 10 μm or larger per 1 mm 2 of the sample surface and evaluated by the following criteria.

-   -   Good: number of cracks is 10 or less     -   Fair: number of cracks is more than 10 and 50 or less     -   Poor: number of cracks is more than 50

(Haze Value)

After the sheet-shape injection molded article was allowed to stand at 60° C. for 24 hours, the sheet was dipped in a quartz cell in which pure water was put by using a hazemeter (trade name: NDH7000SP, manufactured by NIPPON DENSHOKU INDUSTRIES Co., Ltd.) according to JIS K 7136, and the haze value was measured.

(Load Deflection Rate at 80° C.)

After the sheet-shape injection molded article was allowed to stand at 60° C. for 24 hours, a test piece of 80 mm×10 mm was cut out from the injection molded article and heated in an electric furnace at 100° C. for 20 hours. Except for using the obtained test piece, the test was carried out according to a method described in JIS K-K 7191-1 using a heat distortion tester (manufactured by YASUDA SEIKI SEISAKUSHO, LTD.) under the conditions of at a test temperature of 30 to 150° C., a temperature-increasing rate of 120° C./hour, a bending stress of 1.8 MPa and a flatwise method. The load deflection rate was determined by the following formula. A sheet having a low load deflection rate at 80° C. is excellent in the rigidity on heating.

Load deflection rate (%)=a2/a1×100

-   -   a1: the test piece thickness before test (mm)     -   a2: the amount of deflection at 80° C. (mm)

(Tensile Creep Test)

The tensile creep strain was measured by using TMA-7100 manufactured by Hitachi High-Tech Science Corporation. From the sheet-shape injection molded article (40 mm×40 mm×0.5 mmt), a sample of 2 mm in width and 22 mm in length was prepared. The sample was mounted on the measurement jig with a 10 mm distance between jigs. A load was applied to the sample such that the load on the cross-section was 3.32 N/mm², the sample was allowed to stand at 200° C., and the displacement (mm) of the length of the sample from the time point 70 min after the start of the test until the time point 1,320 min after the start of the test was measured to thereby calculate the proportion (tensile creep strain (%)) of the displacement of the length (mm) to the length of the initial sample length (10 mm). A sheet having a small tensile creep strain (%) measured under the condition of 200° C. and 1,320 min hardly elongates even when a tensile load is applied in a high temperature environment for a long time and is excellent in the long-time tensile creep property.

(Electrolytic Solution Permeability)

The sheet-shape injection molded article was allowed to stand at 60° C. for 24 hours, and then a test piece was prepared from the injection molded article. 5.5 g of dimethyl carbonate (DMC) was put in a test cup (permeation area: 7.065 cm 2), and the test cup was covered with the sheet-shape test piece; and a PTFE gasket was pinched and fastened to hermetically close the test cup. The sheet-shape test piece was brought into contact with the DMC, and held at a temperature of 60° C. for 60 days, and thereafter, the test cup was taken out and allowed to stand at room temperature for 1 hour; thereafter, the amount of the mass lost was measured. The electrolytic solution permeability (g/m²) was determined by the following formula.

Electrolytic solution permeability (g/m²)=amount of mass lost (g)/permeation area (m²)

(Methyl Ethyl Ketone (MEK) Permeability)

The sheet-shape injection molded article was allowed to stand at 60° C. for 24 hours, and then a sheet-shape test piece was prepared from the injection molded article. 10 g of MEK was put in a test cup (permeation area: 12.56 cm 2), and the test cup was covered with the sheet-shape test piece; and a PTFE gasket was pinched and fastened to hermetically close the test cup. The sheet-shape test piece was brought into contact with the MEK, and held at a temperature of 60° C. for 60 days, and thereafter, the test cup was taken out and allowed to stand at room temperature for 1 hour; thereafter, the amount of the mass lost was measured. The MEK permeability (g/m²) was determined by the following formula.

MEK permeability(g/m²)=amount of mass lost(g)/permeation area(m²)

(Abrasion Test)

The sheet-shape injection molded article was allowed to stand at 60° C. for 24 hours, and then used as a test piece. The test piece was fixed on a test bench of a Taber abrasion tester (No. 101 Taber type abrasion tester with an option, manufactured by YASUDA SEIKI SEISAKUSHO, LTD.) and the abrasion test was carried out at a test piece surface temperature of 150° C. and a load of 500 g, using an abrasion wheel CS-10 (rotationally polished in 20 rotations with an abrasive paper #240) and at a rotation rate of 60 rpm by using the Taber abrasion tester. The weight of the test piece after 1,000 rotations was measured, and the same test piece was further subjected to the test of 8,000 rotations and thereafter, the weight thereof was measured. The abrasion loss was determined by the following formula.

Abrasion loss (mg)=M1−M2

-   -   M1: the weight of the test piece after the 1,000 rotations (mg)     -   M2: the weight of the test piece after the 8,000 rotations (mg)

(60,000 Times Tensile Strength Retention Ratio)

The 60,000 times tensile strength retention ratio was measured by using a fatigue testing machine MMT-250NV-10 manufactured by Shimadzu Corporation. By using the sheet-shape injection molded article and an ASTM D1708 micro dumbbell, a dumbbell-shape sample (thickness: 2.4 mm, width: 5.0 mm, measurement section length: 22 mm) was prepared. The sample was mounted on a measurement jig, and the measurement jig was installed in a constant-temperature vessel at 150° C. in a state where the sample was mounted. The tension in the uniaxial direction was repeated at a stroke of 0.2 mm and a frequency of 100 Hz, and the tensile strength for each tension (the tensile strength when the stroke was +0.2 mm) was measured. The 60,000 times tensile strength retention ratio was calculated from the measured value according to the following formula.

times tensile strength retention ratio (%)=tensile strength(60,000 times)(mN)/tensile strength(5,000 times)(mN)×100

The 60,000 times tensile strength retention ratio is the ratio of the tensile strength when repeated loads are applied 60,000 times to the tensile strength when repeated loads are applied 5,000 times. An injection molded article having a high 60,000 times tensile strength retention ratio retains the initial tensile strength even after a load is applied 60,000 times, and is excellent in the deterioration resistance to repeated loads.

(NMP Immersion Crack Test)

The sheet-shape injection molded article was punched out by using a rectangular dumbbell of 13.5 mm×38 mm to obtain three test pieces. A notch was formed on the middle of a long side of each obtained test piece according to ASTM D1693 by a blade of 19 mm×0.45 mm. The three notched test pieces and 25 g of N-methylpyrrolidone (NMP) were put in a 100 ml portable reactor (TVS1, manufactured by Taiatsu Glass Kogyo) and heated in an electric furnace at 150° C. for 20 hours, and thereafter, notched test pieces were taken out. Then, the three notched test pieces were mounted on a stress crack test jig according to ASTM D1693, and heated in an electric furnace at 200° C. for 24 hours; thereafter, the notches and their vicinities were visually observed and the number of cracks was counted. A sheet having no crack generated is excellent in the heat distortion resistance even after immersion in a chemical solution.

-   -   Good: the number of cracks was 0     -   Poor: the number of cracks was 1 or more

The above results are shown in Table 4 and Table 5.

TABLE 4 Amount of fluorine Amount ions of metal Tensile dissolving dissolving Ozone creep Electrolytic Cylinder out out exposure strain at solution MEK Type of temperature (Water) (HF) test 200° C. permeability permeability copolymer (° C.) (μg/m²) (μg/m²) 90 days (%) (g/m²) (g/m²) Experimental Synthesis 395 4331 28.6 Good 2.36 271 77.7 Example 1 Example 5 Experimental Synthesis 390 3169 14.1 Good 2.49 267 77.6 Example 2 Example 6 Experimental Synthesis 390 2324 9.4 Good 2.62 267 77.2 Example 3 Example 7 Experimental Synthesis 385 3697 12.6 Good 2.79 265 76.8 Example 4 Example 8 Experimental Synthesis 385 3585 913.3 Fair — — — Example 5 Example 8 Experimental Synthesis 400 7078 28.5 Fair — — — Example 6 Example 8 Comparative Synthesis 390 2747 12.0 Poor 2.14 261 74.6 Example 1 Example 1 Comparative Synthesis 390 4014 19.2 Good 3.69 287 80.8 Example 2 Example 2 Comparative Synthesis 395 4331 28.6 Good 2.36 285 80.7 Example 3 Example 3 Comparative Synthesis 390 26323 107.8 Poor 2.69 288 80.8 Example 4 Example 4 Comparative Synthesis 385 2092 8.9 Poor 2.79 256 74.7 Example 5 Example 9

TABLE 5 Amount of 60.000 fluorine Amount Times ions of metal tensile Load Cylinder dissolving dissolving Ozone Abrasion strength deflection temper- out out exposure loss at retention rate NMP Type of Injection ature (Water) (HF) test Haze 150° C. ratio at 80° C. immersion copolymer moldability (° C.) (μg/m²) (μg/m²) 90 days value (%) (%) (%) crack test Experimental Synthesis 1 390 3752 25.0 Good 23.4 41.1 93.6% 60% Good Example 7 Example 5 Experimental Synthesis 2 390 3106 13.8 Good 23.6 43.1 94.1% 62% Good Example 8 Example 6 Experimental Synthesis 2 390 2278 9.2 Good 23.4 45.2 94.8% 63% Good Example 9 Example 7 Experimental Synthesis 2 390 4706 11.1 Good 23.6 45.5 96.2% 65% Good Example 10 Example 8 Comparative Synthesis 2 390 2692 11.7 Poor 26.0 47.6 91.5% 55% Poor Example 6 Example 1 Comparative Synthesis 2 390 3934 19.2 Good 20.8 41.0 105.7%  76% Good Example 7 Example 2 Comparative Synthesis 0 390 3752 25.0 Good 26.6 37.4 94.0% 62% Good Example 8 Example 3 Comparative Synthesis 2 390 25796 105.7 Poor 23.6 44.2 95.4% 64% Good Example 9 Example 4 Comparative Synthesis 2 390 3451 14.9 Poor 25.6 47.8 96.6% 65% Poor Example 10 Example 9

Experimental Examples 11 to 14 and Comparative Examples 11 to 15 (Preparation of T-Type Joint)

T-type joints having a shape shown in the FIGURE were prepared by injection molding the copolymers of Synthesis Examples 1 to 9 as in Experimental Example 1, except for changing the maximum temperature of the cylinder to 390° C., the mold temperature to 160° C., and the injection speed to 8 mm/s, and changing the mold. The mold used was a mold (T-type joint, 20 mm in outer diameter, 16 mm in inner diameter, 2 mm in thickness, 60 mm in overall length, 35 mm in overall height, side gate at branched section) Ni plated on HPM38.

By using the T-type joints obtained in Experimental Examples and Comparative Examples, the amount of fluorine ions dissolving out and the amount of metal dissolving out were measured by the method described above. The results are shown in Table 6.

The T-type joints obtained in Experimental Examples and Comparative Examples were evaluated by the following method. The results are shown in Table 6.

(Ozone Exposure Test)

Ozone gas (ozone/oxygen=10/90 capacity %) generated in an ozone generation apparatus (trade name: SGX-A11MN (revised), manufactured by SUMITOMO PRECISION PRODUCTS Co., Ltd.) was connected to a container made of PFA in which ion-exchange water was put, bubbled into the ion-exchange water to add water vapor to the ozone gas, and thereafter, passed through a cell made of PFA in which the T-type joint was put at 0.7 liter/min at room temperature, thereby exposing the sample to wet ozone gas. The sample was taken out 90 days after the start of the exposure, the surface was gently rinsed with ion-exchange water, and thereafter, the portion with a depth of 5 to 200 μm from the sample surface was observed using a transmission type optical microscope at a magnification of ×100 and photographed with a standard scale, and the number of cracks having a length of 10 μm or larger per 1 mm 2 of the sample surface and evaluated by the following criteria.

-   -   Good: number of cracks is 10 or less     -   Fair: number of cracks is more than 10 and 50 or less     -   Poor: number of cracks is more than 50

(Evaluation of Electrolytic Solution Swelling Property)

The T-type joint was immersed in dimethylcarbonate (DMC) at 80° C. for 30 days and cooled to room temperature, and then the T-type joint was taken out, DMC with which the surface of the formed article was wet was blown with an air gun, and thereafter, the weight of the T-type joint was measured. The rate of change (ppm by mass) of the weight after immersion relative to the weight before immersion was calculated.

(Evaluation of Joint Forming)

1. Inner Surface Roughness of Hollow Near Gate

The roughness of the inner wall on the periphery of a position in the joint corresponding to the gate section of the mold (position A shown in the FIGURE) was visually checked, and evaluated by the following criteria.

-   -   Good: without surface roughness     -   Poor: with surface roughness

2. Roundness of connection section in front of gate of T shape

The roundness of the inner diameter of the connection section in front of the gate was measured. The inner diameter of the connection section (connection section B shown in the FIGURE) positioned in front of the position in the joint corresponding to the gate section of the mold (position A shown in the FIGURE) was measured at four points for every 45° by setting a direction parallel with the horizontal line of the T shape as the starting point, thereby measuring the maximum inner diameter Dmax and the minimum inner diameter Dmin. The roundness was calculated from the obtained measured values according to the formula, roundness=(Dmax−Dmin)/2, and evaluated by the following criteria.

-   -   Good: roundness is less than 0.05     -   Poor: roundness is 0.05 or more

3. Cobwebbing

Injection molding for preparation of T-type joints was repeated, and when molding was continuously carried out 100 times, the presence or absence of fibrous threads which cause cobwebbing in the appearance was observed.

-   -   Good: no poor appearance of fibrous threads     -   Poor: one or more poor appearances of fibrous threads

The results of the above measurements are shown in Table 6.

TABLE 6 Amount Electro- of fluorine Amount lytic Evaluation of joint forming ions of metal solution Inner dissolving dissolving Ozone swelling surface Roundness Cylinder out out exposure test roughness of Type of temperature (Water) (HF) test (ppm by of hollow connection Cob- copolymer (° C.) (μg/m²) (μg/m²) 90 days mass) near gate section webbing Experimental Synthesis 390 3717 24.9 Good 3652 Good 0.048 Good Good Example 11 Example 5 Experimental Synthesis 390 3105 13.8 Good 3603 Good 0.045 Good Good Example 12 Example 6 Experimental Synthesis 390 2273 9.2 Good 3603 Good 0.042 Good Good Example 13 Example 7 Experimental Synthesis 390 4654 11.0 Good 3598 Good 0.038 Good Good Example 14 Example 8 Comparative Synthesis 390 2673 11.6 Poor 3543 Good 0.050 Poor Good Example 11 Example 1 Comparative Synthesis 390 3977 19.3 Good 3912 Good 0.035 Good Poor Example 12 Example 2 Comparative Synthesis 390 3728 25.0 Good 3869 Poor 0.060 Poor Good Example 13 Example 3 Comparative Synthesis 390 25819 105.2 Poor 3945 Good 0.043 Good Good Example 14 Example 4 Comparative Synthesis 390 3399 14.7 Poor 3484 Good 0.044 Good Good Example 15 Example 9 

1. An injection molded article comprising a copolymer comprising tetrafluoroethylene unit and a fluoro(alkyl vinyl ether) unit, wherein a content of the fluoro(alkyl vinyl ether) unit of the copolymer is 3.9 to 4.8% by mass with respect to the whole of the monomer units, a melt flow rate at 372° C. of the copolymer is 11.0 to 19.0 g/10 min, a melting point of the copolymer is 296 to 305° C., and an amount of fluorine ions dissolving out from the injection molded article into water is 7,500 μg/m² or lower.
 2. The injection molded article according to claim 1, wherein the amount of fluorine ions dissolving out from the injection molded article into water is 5,500 μg/m² or lower.
 3. The injection molded article according to claim 1, wherein an amount of metal dissolving out from the injection molded article into 50% by mass hydrofluoric acid is 200 μg/m² or lower.
 4. The injection molded article according to claim 1, wherein the fluoro(alkyl vinyl ether) unit of the copolymer is perfluoro(propyl vinyl ether) unit.
 5. The injection molded article according to claim 1, wherein the content of the fluoro(alkyl vinyl ether) unit of the copolymer is 4.1 to 4.5% by mass with respect to the whole of the monomer units.
 6. The injection molded article according to claim 1, wherein the melt flow rate at 372° C. of the copolymer is 12.0 to 17.6 g/10 min.
 7. The injection molded article according to claim 1, wherein the total number of —CF═CF₂, —CF₂H, —COF, —COOH, —COOCH₃, —CONH₂ and —CH₂OH of the copolymer is 20 or less per 10⁶ main-chain carbon atoms.
 8. The injection molded article according to claim 1, wherein the injection molded article is a female joint.
 9. A method for producing the injection molded article according to claim 1, comprising injection molding the copolymer using an injection molding machine provided with a cylinder and a screw accommodated in the cylinder, to obtain the injection molded article.
 10. The production method according to claim 9, wherein the temperature of the copolymer in the cylinder is adjusted to 385 to 395° C.
 11. The production method according to claim 9, wherein a Ni plated cylinder or a cylinder formed of a Ni-based alloy is used as the cylinder, and a screw formed of a Ni-based alloy and provided with a smear head on a head end is used as the screw. 